Production of Ferro- Manganese Jun19

Production of Ferro- Manganese...

Production of Ferro- Manganese Ferro-manganese (Fe-Mn) is an important additive used as a deoxidizer in the production of steel. It is a master alloy of iron (Fe) and manganese (Mn) with a minimum Mn content of 65 %, and maximum Mn content of 95 %. It is produced by heating a mixture of the oxides of Mn (MnO2) and iron (Fe2O3) with carbon (C) normally as coke or coal. Fe-Mn in a blast furnace (BF) with considerably higher Mn content than was possible earlier was first produced in 1872 by Lambert Von Pantz. The Fe-Mn produced had 37 % Mn instead of 12 % being obtained earlier. Metallurgical grade Mn ores having Mn content higher than 40 % are usually processed into suitable metallic ferro- alloy forms by pyro-metallurgical processes, which are very similar to the iron pyro-metallurgical processes. In its production process, a mixture of Mn ore, reductant (a form of C) and flux (CaO) are smelted at a temperature which is higher than 1200 deg C to enable reduction reactions and alloy formation. Standard grades of Fe-Mn can be produced either in a BF or in an electric submerged arc furnace (SAF). The electric SAF process, however, is far more flexible than the BF process, in that slags can be further processed to Si-Mn and refined Fe-Mn. The choice of process is also dependent on the relative price of electric power and coke. In a three-phase SAF, the electrodes are buried in the charge material. The raw materials are heated and the Mn oxides pre-reduced by hot carbon mono oxide (CO) gas form the reaction zones deeper in the furnace. The exothermic reactions contribute favourably to the heat required. Efficient production of HC Fe-Mn depends on the degree of pre-reduction which occurs...

Silico- Manganese

Silico- Manganese Silico-manganese (Si-Mn) is a metallic ferro alloy which is being used to add both silicon (Si) and manganese (Mn) as ladle addition during steelmaking. Because of its lower carbon (C) content, it is a preferred ladle addition material during making of low carbon steels. Si-Mn is a ferroalloy composed principally of Mn, Si, and Fe (iron), and normally contains much smaller proportions of minor elements, such as C, phosphorus (P), and sulphur (S). The ferroalloy is also sometimes referred to as ferro-silicon-manganese. Both Mn and Si play an important role in the manufacturing of steel as deoxidizing, desulphurizing, and alloying agents. Si is the primary and more powerful deoxidizer. Mn is a milder deoxidizer than Si but enhances the effectiveness of the latter due to the formation of stable manganese silicates and aluminates. It also serves as desulphurizer. Mn is used as an alloying element in almost all types of steel. Of particular interest is its modifying effect on the iron-carbon (Fe-C) system by increasing the hardenability of the steel. There are two families of Mn alloys one is called Si-Mn while the other is known as ferro-manganese (Fe-Mn). Si-Mn adds additional silicon in liquid steel which is a stronger deoxidizer and which also helps to improve some mechanical properties of steel. In each family, content of C can be controlled and lowered when producing low C grades. Around 93 % of all the Mn produced is in the form of Mn ferroalloys consists of the Fe-Mn grades and the Si-Mn grades. The Fe-Mn grades are high carbon (HC), medium carbon (MC), low-carbon (LC) and very low carbon (VLC), whereas the Si-Mn grades include medium carbon (MC) and low carbon (LC). The steel industry is the only consumer of these alloys. However...

Stages during the Development of Management Concepts...

Stages during the Development of Management Concepts Management is considered to be the process of getting planned things implemented through and with people within the available resources of the organization. Management consists of accomplishment of predetermined objectives through planning and directing of efforts and the organizing and employing of the human and material resources. Management is an approach which enables the realization of the desired results (generally expressed in terms of performance) by taking actions to achieve those results and by dealing with the dangers brought in by external and internal factors (environment) within the organization. Development of the management concepts has taken place in several stages. During these stages, different approaches for the management concepts have been developed. These stages provide the information about the approach which was predominant during the period of the stage. These management approaches have been developed and tested over time. Elements from these approaches which have been proven successful can be taken and integrated to arrive at a unified system of management practice to suit a particular situation in an organization. During the study of the stages of the management concepts, it can be seen that there is non-linearity and every stage involves active interplay of components which cannot be separated into distinct elements. Further, since there is continuous evolvement of management processes, their identification with a certain stage is a bit vague, though there are some practices which are dominating during each stage. Though, it is difficult to predict the timings for these practices, there are periods in the stage when the specific practice has been developed and applied with sufficient regularity. These regular practices of the various stages are given below. Stage of scientific management The basis of the scientific management is considered to be the...

Production of Silico-Manganese in a Submerged Arc Furnace Jun09

Production of Silico-Manganese in a Submerged Arc Furnace...

Production of Silico-Manganese in a Submerged Arc Furnace Silico-manganese (Si-Mn) is an alloy used for adding both silicon (Si) and manganese (Mn) to liquid steel during steelmaking at low carbon (C) content. A standard Si-Mn alloy contains 65 % to 70 % Mn, 15 % to 20 % Si and 1.5 % to 2 % C. Si-Mn alloy grades are medium carbon (MC) and low carbon (LC). The steelmaking industry is the only consumer of this alloy. Use of Si-Mn during steelmaking in place of a mix of high carbon ferro-manganese (Fe-Mn) alloy and ferro-silicon (Fe-Si) alloy is driven by economic considerations. Both Mn and Si are crucial constituents in steelmaking. They are used as deoxidizers, desulphurizers and alloying elements. Si is the primary deoxidizer. Mn is a milder deoxidizer than Si but enhances the effectiveness due to the formation of stable manganese silicates and aluminates. It also serves as desulphurizer. Manganese is used as an alloying element in almost all types of steel. Of particular interest is its modifying effect on the iron-carbon (Fe-C) system by increasing the hardenability of the steel. Si-Mn is produced by carbo-thermic reduction of oxidic raw materials in a three-phase, alternating current (AC), submerged arc furnace (SAF) which is also being used for the production of Fe-Mn. Operation of the process for the Si-Mn production is often more difficult than the Fe-Mn production process since higher process temperature is needed. The common sizes of the SAF used for the production of Si-Mn are normally in the range 9 MVA to 40 MVA producing 45 tons to 220 tons of Si-Mn per day. In the carbo-thermic reduction of oxidic raw materials, heat is just as essential for reduction as C is, due to the endothermic reduction reactions and a...